Right off the bat, please note: I have researched all available post, threads, videos, and comments found relating Bambu PETG-CF and the X1C. Some are not included in here as they either are redundant (same user posting the same info) or they do not provide sufficient evidence for the settings Plea…

I appreciate you reading it. The format is a bit janky, but it was the best I found after trying a few options. As for the PETG-CF, I would absolutely say that a large amount of people have issues with it. However, I think there is a large amount who do not due to their print geometry and time. It …

Have you come across this article? It is the most comprehensive one I have found about PETG. It might have a suggestion you haven’t tried yet. [image] PETG Filament - Complete 3D Printing Guide [Updated for 2022] — STANDARD... Your complete guide to 3D printing with PETG, covering best…

Problem is not PETG the focus is on PETG-CF

your response is fair but since it’s only a max of 15% carbon fiber and the material still being mainly PETG I think we shouldn’t dismiss any tips for PET-G that quickly :). Anyway anything that is PETG always has had the same issues in general with clinging to the nozzle. This is why E3D came out …

Nice thread but I dispute the ‘not proven’ on the G29.1 Z0.03 PETG has had issues sticking to the nozzle since the beginning of time. And raising the Z offset works every time. I spent hundreds of hours trying to find a solution to PETG epic ball fails, random torn surfaces, etc. It was a random co…

Ok in my situation automatic arrange with object rotation helps a lot. With that is not possible print some separate details.

I will respond to @SimEyeSee here as well since these are connected. While I have not see that article before, I read over it and many of the solutions are similar to what I posted. The main reoccurring one being a Z- Offset. To @LagoaLabs , you are correct. While the CF content of Bambu’s filament …

I should have worded that better. By “not proven”, I meant that is not the singular cause and solution to the issue. I actually found going up to 0.04 to be a pretty strong improvement. That, coupled with 20% Rectilinear infill, concentric top/bottom layers, and speed changes to allow for a decent 1…

holy moly! You might be onto to something here! It seems that rectilinear might also not do this as I cannot find anywhere it occurs. That, or it might not be as pronounced. While searching the GCode, I have also found that if interface layers on support are used a new issue can occur. Say you have…

Solution to printing Bambu PETG-CF with X1C (.4 and .6 Nozzle)

Bambu Lab X Series Bambu Lab X1C

wiremeup October 23, 2023, 3:05am 9

I’d like to link to a post I made on a previous thread. I believe I have discovered a bug perhaps in the slice or maybe its just poor choices in general. Gyroid + infill combination = incorrect infill gcode.