Sorry for the somewhat noob question… it seems that the Engineering plate is no longer available. I have a project which I will be running in either PAHT-CF or PA6, looking at the filament listing the suggested build plate is the Engineering plate, which is no longer available.
It seems that the new PEI plates are listed as suitable, does anyone have experience in the nylon filaments and which plates work best?
Thanks!
Use the dual side Smooth PEI plate.
1 Like
Thanks Sim! Appreciate the response!
You will want to use glue not so much as a guarantee of layer adhesion but as a release liner. The glue itself will help anchor the model, but after it cools down or if you place it in the freezer before removal, you will find that the model snaps off much easier because the glue becomes the weak link after cooldown.
To bear witness to this. Look what happened to our poor comrade in this thread when using PETG. But any high temp filament is subject to this hyper-aggressive stiction.