Hi all, i have an A1, and A1 mini, i have just bought some spools of Anycubic black, and i´m having problems with tuning the filament, when i do the calibration al surfaces seems to be shiny, like over extrusion and when they aren´t, they have under extrusion, any one with this problem??. I have tried at 210 temp, after a tower, also tried with 205 and now i´m trying 200.
May want to show some pics if you can. Will help out.
Hi,
I’ve had the fewest problems with Anycubic’s PLA+.
I’m currently printing with the Kobra 3 at 230 degrees, which is interesting since only up to 210 is recommended.
But it’s working quite well.
Try that with the Bambu.
im now testing 220 Xd, the next will be 230, thanks
Could just run a temp tower.
The Kobra 3 is a bit faster.
Maybe that’s why the filament handles 230 degrees.
It seems like 230 degrees is standard for the Kobra 3.
Definitely keep an eye on the printer while doing that.
1 Like
Sorry, but yesterday was crazy, this is what a mean, i have tried with the best result 200 degrees and changing cooling exposure time (sorry i have bambustudio in spanish and i’m not in front of computer). But still that little glossy in the borders. I have flow at 94 and tried with 92 and 93
That was my experience as well, especially with PLA Matte. Anything above 200 degrees caused stringing and bed adhesion issues.
This is an old post but I am also having problems with black pla basic from anycubic.. it is seemingly random but about 50% of my prints shrink and warp until they are unrecognizable- with the bottom layer lifting to above the level of the current top layer, resulting in the nozzle scraping material away instead of laying material down. again- it’s totally random.. sometimes the object comes out perfect, sometimes it warps to extreme levels without any discernable rhyme or reason.. i have tried everything i can think of- different speeds, different temps, different cooling settings. i have gone through all the calibration tests in orca and everything looks fine. i am currently running a spool through a drying cycle and will try that but so far it is already measuring reasonably dry.. if anyone can help i would be much appreciative!